MHN™ Self-piercing clinch nuts for thin sheet applications
Nuts
Application area
- Can be universally used for component thicknesses from 0.7 to 3.5 mm and tensile strengths of up to 700 MPa
- Suitable for a wide range of high dynamic, static and impact load conditions
- Suitable for use where threaded fittings need to be resistant to high axial forces
- Designed to be a self-piercing nut
- Suitable for use with surface-treated, galvanized or painted components
Technical Characteristics
- Thread sizes: M6 to M12
- P.C. 10 (standard)
- Resistance to corrosion in accordance with the customer’s requirements
- No adverse effects on the joint or function of the thread; no damage due to weld spatters
- High resistance to twist and ejection forces, even for thin sheet metals
- Nut positioning tolerance ranges can be halved as compared to welding methods
- Straightforward, in-process and non-destructive quality testing possible by worker instead of elaborate destructive tests
Unit of Measure
Items |
![]() MHN06 MHN™ Clinch Nuts |
![]() MHN08 MHN™ Clinch Nuts |
![]() MHN10 MHN™ Clinch Nuts |
![]() MHN12 MHN™ Clinch Nuts |
||||
Type | N/A Clinch Nuts | |||||||
Material | N/A DIN EN 20 898-2 | |||||||
Thread Size | N/A M6x1.00 | N/A M8x1.25 | N/A M10x1.5 | N/A M12x1.75 | ||||
Thread Tolerance | N/A 6E DIN 13-20 * | |||||||
Property Class | N/A 10 DIN EN ISO 898-2 * | |||||||
Surface Coating | N/A Zinc-Nickel * | |||||||
Material Application Range | N/A Aluminum - HSLA | |||||||
Panel Thickness Range | N/A 0.70 - 2.50 mm | N/A 0.70 - 2.50 mm | N/A 1.00 - 3.00 mm | N/A 1.50 - 3.50 mm | ||||
Fastening Method | N/A Clinch | |||||||
Panel Preparation | N/A Self-Pierce | |||||||
Nut Outside Diameter Ød1 ** |
N/A
18.3 mm
|
N/A
20.5 mm
|
N/A
24 mm
|
N/A
28 mm
|
||||
W (Flats) | N/A 17.8 mm | N/A 20 mm | N/A 23.4 mm | N/A 27.2 mm | ||||
Nut Thickness H | N/A 4.65 mm | N/A 6 mm | N/A 7.6 mm | N/A 7.9 mm | ||||